Vintex Steel Engg. Co. is a reliable Valve Supplier in Muharraq, offering a wide selection of precision-engineered valves designed to regulate flow efficiently and deliver long-lasting performance. The valves are manufactured using premium quality raw materials, which enhance their strength and allow them to perform effectively even under extreme pressure and temperature conditions. Each product is developed in accordance with industry standards to ensure durability, safety, and consistent performance across various applications.
Valves Supplier, Valves Exporter in Muharraq
As a dependable Valves Supplier in Muharraq, the company provides a broad range of industrial valves suitable for numerous applications and project requirements. With a strong commitment to reliability and product quality, Vintex Steel Engg. Co. ensures that valves are delivered on time to support smooth project operations. These valves are widely used in multiple industries where accurate flow control is essential, making them suitable for diverse industrial and commercial environments.
Material Specification Chart Of Valves
| Valves | Specifications |
| Size Range | 1/2″ to 24″ |
| Pressure Rating | 150#, 300#, 600#, 800#, 900#, 1500# |
| Certifications | IBR, CE, ATex, FAT, SAT, etc. |
| Stainless Steel | ASTM A351 CF8/CF8M |
| Carbon Steel | ASTM A216 WCA, WCB, WCC |
Most Commonly used Valves Types
Gate Valves
Diaphragm Valves
Globe Valves
Ball Valves
Butterfly Valves
Plug Valves
Foot Valves
Strainer Valves
Valves Chemical Composition
| Material / Spec | C | Mn | Si | P ≤ | S ≤ | Cr | Ni | Mo | Cu | Other |
|---|---|---|---|---|---|---|---|---|---|---|
| Carbon Steel A105/A350 | ≤ 0.30% | 0.60–1.35% | 0.15–0.30% | 0.035% | 0.040% | ≤ 0.30% | ≤ 0.40% | ≤ 0.12% | 0.04% max | —s.com+8 |
| ASTM A694 CS | similar to A105 | — | — | — | — | — | — | — | — | — |
| CF8 / 304 (A351) | ≤ 0.08% | ≤ 2.0% | ≤ 1.0% | ≤ 0.045% | ≤ 0.03% | 18–21% | 8–11% | — | — | — |
| CF3 / 304L | ≤ 0.035% | ≤ 2.0% | ≤ 1.0% | ≤ 0.045% | ≤ 0.03% | 17–19% | 8–12% | — | — | — |
| CF8M / 316 | ≤ 0.08% | — | — | ≤ 0.045% | ≤ 0.03% | 18–21% | 8–11% | 2–3% | — | — |
| CF3M / 316L | ≤ 0.035% | — | — | ≤ 0.045% | ≤ 0.03% | 17–19% | 8–12% | 2–3% | — | — |
| 17‑4 PH (UNS S17400) | ≤ 0.07% | ≤ 1.0% | ≤ 1.0% | ≤ 0.04% | ≤ 0.03% | 15.0–17.5% | 3–5% | — | 3–5% | Nb/Ta 0.15–0.45% |
| Alloy 20 (UNS N08020) | ≤ 0.06% | ≤ 2.0% | ≤ 1.0% | — | — | 19–21% | 32–38% | 2–3% | 3–4% | Nb ≤1%, Fe bal. |
| 904L (UNS N08904) | ≤ 0.02% | ≤ 2.0% | ≤ 1.0% | — | — | 19–23% | 23–28% | 4–5% | 1–2% | Fe bal. |
| AL‑6XN (UNS N08367) | ≤ 0.03% | ≤ 2.0% | ≤ 1.0% | ≤ 0.04% | ≤ 0.03% | 20–22% | 23.5–25.5% | 6.0–7.0% | — | N 0.18–0.25% |
Valves Mechanical Properties
| Material / Spec | Yield Strength (min) | Tensile Strength (min) | Elongation | Hardness (HB / HRB) |
|---|---|---|---|---|
| ASTM A351 CF8 (Cast 304 SS) | 28 ksi (193 MPa) | 65 ksi (448 MPa) | 35 % | ~140 HBen.wikipedia.org+12 |
| ASTM A351 CF8M (Cast 316 SS) | 30 ksi (207 MPa) | 70 ksi (483 MPa) | 30 % | ~156–170 HB; HRB ≤ 85 |
| WCB Carbon Steel (A216) | 36 ksi (248 MPa) | 70 ksi (483 MPa) | 22 % | — |
| ASTM A217 WC6 (Chrome‑Moly) | 40 ksi (276 MPa) | 70 ksi (483 MPa) | 20 % | — |
| ASTM A217 C5 (Alloy Steel) | 60 ksi (414 MPa) | 90 ksi (620 MPa) | 18 % | — |
| Cast CA6NM (Cast 415 SS) | 80 ksi (552 MPa) | 110 ksi (758 MPa) | 17 % | — |
| Cast 17‑4 PH (CB7Cu‑1) | 100 ksi (690 MPa) # | 135 ksi (931 MPa) # | 9 % # | — |
| CF3M / 316L Cast SS | 30 ksi (207 MPa) | 75 ksi (517 MPa) | 30–35 % | — |
| Hastelloy C276 | 52 ksi (355 MPa) | 115 ksi (790 MPa) | 40 % | — |
| Hastelloy C22 | 45 ksi (310 MPa) | 100 ksi (690 MPa) | 45 % | — |
| Incoloy 800 / 800H | 30 ksi (205 MPa) | 75 ksi (520 MPa) | 30 % | — |
| Incoloy 825 | 32 ksi (220 MPa) | 80 ksi (550 MPa) | 30 % | — |
Valves Uses and Application
- Nuclear Energy Sector
- Offshore & Chemical Industry
- Engineering & Aerospace Industry
- Automotive industry
- Oil & Gas Industries
- Power Generation
- Architectural Trim and Molding
- Kitchen Benches, Sinks, Equipment
- Food Processing Equipment